  4. Welded Layers Microstructure Modification on the Basis of Powder Wire Cr10B4 with addition of Al, Mg

Welded Layers Microstructure Modification on the Basis of Powder Wire Cr10B4 with addition of Al, Mg

Andriy Voitovych andrsibox [at] gmail.com
Roman Mykhalskyi
Roman Vlakh
  1. Department of Welding, Hardware Diagnosis and Restoration, Lviv Polytechnic National University, Ukraine, Lviv, S. Bandery street 12.
Abstract 

The welded layers formed of powder wires PW Cr10B4, PW Cr10B4Al2, PW Cr10B4AlMg were investigated in the course of work. It was defined that Al, Mg applications influence the microstructure grinding and rounding carboboride inclusions. Abrasive wear resistance of the weld materials under the condition of outwearing by a fixed abrasive, unfixed abrasive, as well as shock load, was detected. It was determined that wear resistance of the welded layers with PW Cr10B4AlMg at shock load was 3.5 time higher than that of other weld materials. Degradation mechanism of the welded layers PW Cr10B4AlMg is malleable.

Keywords 
welded layers
microstructure modification
powder wire
wear-resistance
surface
References 
  1. Добровольский А. Г. Абразивная износостойкость материалов / Добровольский А. Г., Кошеленко П. И // Cправочное пособие. – К.: “Теника”, 1989. – 128 с.
  2. Yuksel N. Wear behavior–hardness–microstructure relation of Fe–Cr–C and Fe–Cr–C–B based hardfacing alloys / Yuksel N., S_ahin S // Materials and Design 58 (2014) 491–498.
  3. Лившиц. Л. С. Металловедение для сварщиков (сварка сталей) / Машиностроение, 1979. – 253 с.
  4. Buchely M. The effect of microstructure on abrasive wear of hardfacing alloys / Buchely M, Gutierrez J, Leon L, Toro A // Wear – 2005 - №259 P. 52–61.
  5. M. Varga. Impact of microstructure on high temperature wear resistance / M. Varga, H. Winkelmann, E. Badisch // Procedia Engineering 10 (2011) 1291–1296.
  6. А. Г. Панов. Влияние микроструктуры фсмг-модификаторов на кристаллизацию и микроструктуру высокопрочных чугунов / А. Г.. Панов // Металлургия и материаловедение № 1(2013) 209 – 219.