Calculated Model for Determining the Subcritical Growth period of CorrosionMechanical Crack in Plate under Long-Term Static and Time Concentrated Quasi-Dynamic Loadings

Ivan Shtoyko ivan.shtoyko [at] gmail.com
  1. Karpenko Physico-Mechanical Institute of the NAS of Ukraine, Ukraine, Lviv, 5, Naukova str.
Abstract 

The calculation model for determining of residual durability of plate with straight corrosion-mechanical crack under long-term static tension and multiple time concentrated quasi-dynamic load is proposed. The model based on the energy approach for a study of delayed crack growth, models of pulsed load applying and the main mechanisms of corrosion-mechanical crack propagation. Based on this model, the dependence of residual life of the plate of X60 pipeline steel on a number of time concentrated quasi-dynamic loadings is investigated. 

References 
  1. A. Y. Krasowsky, A. A. Dolgiy and V. M. Torop, “Charpy testing to estimate pipeline steel degradation after 30 years of operation”, in Proc. “Charpy Centary Conference”, Poitiers, vol. 1, 2001, pp. 489–495.
  2. O. T. Tsyrulnyk et al., “Embrittlement of the steel of an oil-trunk pipeline”, Materials Science, vol. 40, № 2, 2004, pp. 302–304.
  3. O. T. Tsyrulnyk et al., “Hydrogen degradation of steels in gas mains after long periods of operation”, Materials Science, vol. 43, № 5, 2007, pp. 708–717.
  4. H. M. Nykyforchyn and O. T. Tsyrul’nyk, “Specific features of the in-service bulk degradation of structural steels under the action of corrosive media”, Strength of Materials, vol. 41, № 6, 2009, pp. 651–663.
  5. A. Y. Krasowsky, I. V. Lokhman and I. V. Orynyak, “Stress-corrosion failures of main pipelines”, Strength of Materials, vol. 44, № 2, 2012, pp. 129–143.
  6. E. I. Kryzhanivs’kyi, R. S. Hrabovs’kyi and O. M. Mandryk. “Estimation of the serviceability of oil and gas pipelines after long-term operation according to the parameters of their defectiveness”, Materials Science, vol. 49, № 1, 2013, pp. 117–123.
  7. O. E. Andreikiv et al., “Evaluation of the residual lifetime of a section of a main gas pipeline after long term operation”, Material Science, vol. 48, № 2, 2012, pp. 231–238.
  8. O. E. Andreikiv and N. B. Sas, “Strength of thinwalled structural elements with cracks under the conditions of creep”, Material Science, vol. 43, № 2, 2007, pp. 174–182.
  9. O. E. Andreikiv and N. B. Sas, “Fracture mechanics of metal plates under hightemperature creep” Material Science, vol. 42, № 2, 2006, pp. 210–219.
  10. Handbook of Fatigue Crack Propagation in Metallic Structures, A. Carpinteri, Ed. – Elsevier, 1994, vol. 1, 952 p.
  11. O. E. Andreikiv and O. V. Hembara, “Fracture Mechanics and Durability of Metallic Materials in Hydrogen-Containing Media” [in Ukrainian], Kyiv: Naukova Dumka, 2008.
  12. Y. T. Li and R. Wong, “Integral and series representations of the Dirac delta function”, Commun. Pure Appl. Anal., vol. 7, № 2, 2008, pp. 229–247.
  13. N. I. Tym'yak and O. E. Andreikiv, “Evaluation of crack-growth rate under conditions of simultaneous action of static loading and corrosive media”, Materials Science, vol. 31, № 2, 1995, pp. 219−225.
  14. Hembara O. V., Terlets’ka Z. O., Chepil’ O. Ya. Determination of electric fields in electrolyte-metal systems // Material Science, vol. 43, № 2, 2007, pp. 222−229.
  15. M. Elboujdaini, “Initiation of environmentally assisted cracking in line pipe steel”, in 16th European on Fraсture (ECF16th) “Fracture of Nano and Engineering materials and structures”, Alexandropoulos, Greece, July 3-7, 2006. – Dordrecht: Springer, 2006, pp. 1007– 1008.
  16. Z. V. Slobodian, H. M. Nykyforchyn and O. I. Petrushchak, “Corrosion resistance of pipe steel in petroleumwater media”, Material Science, № 3, 2002, pp. 93-96.
  17. Handbook of Fatigue Crack Propagation in Metallic Structures, A. Carpinteri, Ed. – Elsevier, 1994, vol. 2, 1764 p.
  18. H. Nykyforchyn et al., “In service degradation of mechanical and corrosion-mechanical properties of transit gas pipeline steels” in Proc. of 14th international conference Mechanica, Kaunas, Lithuiania, 2009, pp. 278–283.
  19. O. T. Tsyrul’nyk et al., “Influence of operation of KH52 steel on corrosion processes in a model solution of gas condensate”. Material Science, vol. 42, № 5, 2006, pp. 219–229.